Dpto. Odontología

This in vitro study aimed to evaluate the effect of different bonding strategies on the microshear bond strength ( SBS) of luting agents to CAD–CAM composites. Surface scanning electron microscopy (SEM) and spectroscopy by energy-dispersive X-ray spectroscopy (EDS) were performed to analyze the surfaces of the composite before and after bonding treatment. Three CAD–CAM composites were evaluated: Lava Ultimate restorative (LU), Brava Blocks (BR), and Vita Enamic (VE). The LU and BR surfaces were sandblasted using aluminum oxide, while the VE surfaces were etched using a 5% hydrofluoric acid gel according to the manufacturers’ recommendations. All surfaces were subjected to the following bonding strategies (n = 15): adhesive with silane and MDP (ScotchBond Universal, 3M Oral Care, St Paul, MI, USA); adhesive with MDP (Ambar Universal, FGM, Joinville, Brazil); adhesive without silane or MDP (Prime&Bond Elect, Dentsply Sirona, Charlotte, NC, USA), pure silane without MDP (Angelus, Londrina, Brazil), and pure silane with MDP (Monobond N, Ivoclar Vivadent, Schaan, Liechtenstei). Afterwards, tygons were filled with RelyX Ultimate (3M Oral Care), AllCem (FGM), or Enforce (Dentsply Sirona), which were light-cured and subjected to the SBS test. Data were analyzed using two-way ANOVA and Bonferroni’s post hoc test ( = 0.05). Additional blocks (n = 15) were subjected to scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS) before and after the surface treatment. The SBS values on VE surfaces were higher than those observed on LU and BR surfaces (p < 0.001). Silane without MDP (Allcem) promoted the highest SBS values, while silane with MDP (RelyX Ultimate) provided the highest values among all bonding strategies (p < 0.001). Enforce promoted no significant difference in SBS values. SEM and EDS analyses detected noticeable changes to the surface morphology and composition after the surface treatment. The effectiveness of the bonding strategy may vary according not only to the CAD–CAM composite but also to resin cement/bonding agent/silane used.

The aim of the present study was to evaluate the influence of several experimental pretreatment crosslinker solutions on the resin polymer–dentine interface created using a representative universal adhesive system, by means of microtensile bond strength testing ( TBS), nanomechanical properties and ultramorphology confocal laser scanning microscopy (CLSM). Five experimental solutions containing different flavonoids were applied as dentine pretreatment after acid etching. A control pretreatment group containing no flavonoid was also employed. A representative modern universal adhesive was then applied, followed by a 3 mm thick composite built up. Specimens were sectioned into sticks and submitted to a TBS test or nanoindentation analysis along the interface (24 h or 25,000 thermocycles). The ultramorphology of the polymer–resin interface was also evaluated using CLSM. The results were analyzed using two-way ANOVA and Bonferroni’s post hoc test ( = 0.05). All flavonoids improved short- and long-term TBS values (p < 0.01), while only some specific such solutions improved the nanomechanical properties (p < 0.05) and preserved the structural morphology of the interface after aging. Pretreatment of acid-etched dentine using specific flavonoid-containing solutions may be a promising approach to improve both the nanomechanical properties and the durability of modern universal adhesive systems.